In the present work, the sol-gel synthesis method was employed as strategy to obtain a magnetic and mesoporous silica-niobia material. The planned synthesis was based on the hetero-condensation of niobium and silicon alkoxide precursors, in the presence of spherical magnetite particles. The resulting material presented interesting characteristics such as magnetism, large mesopores, in the range from 20 to 50 nm, and 68 m2 g-1 of surface area. These features allowed its use as modifier of carbon paste electrode for p-nitrophenol determination, since niobia has never been used in electrochemical sensors for the determination of nitrophenol compounds. By using differential pulse voltammetry technique, the electrode can be applied in a wide range of p-nitrophenol concentration, from 10 to 490 μmol L-1, with a limit of detection of 1.2 µmol L-1 and sensitivity up to 0.60 µA L µmol-1. The proposed electrode presented good sensitivity and selectivity and it was applied in real water samples.

A mesoporous, high surface area and conductive silica/titania graphite composite modified with chitosan and functionalized with tyrosinase was prepared. The composite was obtained by the sol-gel method and the surface of the resultant material was modified with chitosan solutions containing 5, 10 and 15% by mass. The textural characterization showed that even after modification with chitosan, the composite maintains a pore volume near 0.70 cm3 g-1 and pore diameter between 10 and 50 nm, adequate for enzyme immobilization. The tyrosinase was immobilized on the composite that was modified with 5% chitosan solution. A carbon ceramic electrode was manufactured with this material and was used as an electrochemical biosensor for phenolic compounds, showing low detection limits in the linear range from 40 to 350 µmol L-1 and good sensitivity of 0.284, 0.141 and 0.165 µA µmol-1 L for catechol, dopamine and pyrogallol, respectively. In this composite the enzyme showed to be operative and stable after several months.

We carried out the physico-chemical characterization of Immobead 150, a hydrophobic support for the immobilization of lipases. Thermomyces lanuginosus lipase (TLL) was immobilized on Immobead 150 by multipoint covalent attachment (ImmTLL) and the morphological, textural, structural, thermal, and physico-chemical properties of the support, before and after enzyme immobilization, were investigated. Immobead 150 presents approximately 1,000 µmol of epoxy groups per gram of support, a high hydrophobicity, and good thermal stability. The spherical particles of Immobead 150 present average diameters of 155 µm, specific surface areas of 137 m2 g-1 and pore volumes of 0.37 cm3 g-1, showing pores in the region of the micro and meso sizes. The immobilization process of TLL (150 mg g-1) caused a decrease of the specific area and pore volumes, to 63 m2 g-1 and 0.25 cm3 g-1, respectively, as a result of coating of the support surface by the enzyme molecule. However, the immobilization process did not affect the morphology of the support. The obtained biocatalyst was effective for the syntheses of fatty acid ethyl esters (biodiesel), and of aroma esters, showing yields of 68 and 70%, respectively, similar to commercial preparations used as controls.

Thin films containing silver nanoparticles homogeneously dispersed, with narrow size distribution below 10 nm, were synthesized on flat glass surface, by using an ionic silsesquioxane as stabilizer and crosslinking agent. The films can be prepared without previous functionalization of substrate surfaces and without addition of other components. The films were heat treated up to 200 ºC and characterized by ultraviolet-visible, transmission electron microscopy, atomic force microscopy, thermogravimetric analysis and ellipsometry. The films were thermally stable when heated up to 200 ºC, presenting the same thickness, and maintaining both optical and morphological properties of silver nanoparticles. The antibacterial activity of the films, containing the silver nanoparticles, was evaluated against Staphylococcus aureus by using the film applicator coating method, showing an excellent performance even after the third cycle of sterilization.

This review deals with silica based hybrid materials obtained by the sol-gel method. It involves concepts, classifications and important definitions regarding the sol-gel method that allows obtaining materials with organic and inorganic components dispersed in a molecular or nanometric level. We discuss the properties and characteristics of hybrid materials related to experimental synthesis conditions. We devote a special attention to the nanostructured materials, where the self-organization is imposed by the organic component. Finally, we present some important applications of these materials based on their specific properties.

Uma nova série de amostras de material híbrido à base de sílica, contendo o grupo catiônico amoniopropil ligado na forma pendente, foi obtida usando-se o método sol-gel de síntese, variando-se a razão molar entre o precursor inorgânico e o precursor orgânico. A análise termogravimétrica mostrou que as amostras são termicamente estáveis até 260 ºC. Os resultados obtidos por difratometria de raios X, microscopia eletrônica de transmissão, ressonância magnética nuclear de 29Si e análise elementar são compatíveis com o modelo estrutural de camadas de silsesquioxano com distâncias basais de até 5,4 nm, contendo sílica amorfa no espaço entre as camadas.

An innovative series of silica-based hybrid materials containing pendant cationic ammoniumpropyl groups was obtained using the sol-gel method, by varying the molar ratio of the inorganic and organic precursors. Thermogravimetric analysis showed that samples were thermally stable up to 260 ºC. Results obtained by X-ray diffractometry, transmission electron microscopy, 29Si nuclear magnetic resonance and elemental analysis were compatible with a silsesquioxane layered structural model showing basal distances up to 5.4 nm, containing amorphous silica in the interlayer space.

Nesse trabalho foi estudada a influência do ácido acético na estrutura de poros e na área superficial de sílicas preparadas pelo método sol-gel. Condições experimentais de síntese, tais como temperatura de policondensação e solventes, também foram estudadas. Isotermas de adsorção de N2 das amostras foram classificadas como do tipo 1, típicas de materiais microporosos, o que explica os altos valores de área superficial obtidos. A adição simultânea dos ácidos acético e clorídrico como catalisadores e de acetona como solvente, bem como o emprego de uma temperatura de policondensação de 20 ºC, possibilitaram a preparação de sílicas amorfas com valores de área superficial de até 850 m² g-1. O alto valor de área superficial dessas amostras pode ser explicado principalmente pela microporosidade e também pelo tamanho nanométrico das partículas.

The influence of acetic acid on the pore structure and surface area of silica prepared by the sol-gel method was investigated. Experimental conditions of synthesis, such as gelation temperature and solvents, were also studied. N2 adsorption isotherms of the samples were type 1, typical of microporous materials, explaining the high surface area values (BET) observed. The simultaneous addition of acetic and hydrochloric acids as catalysts and of acetone as solvent, together with the use of a gelation temperature of 20 ºC, made it possible to prepare amorphous silica materials with surface area values up to 850 m² g-1. The high surface area value of these samples could be explained by the microporosity and the nanometric size of the particles.

In this study, the preparation of the xerogel anilinepropylsilica is reported. The ability of the xerogel for extracting Al(III), Cr(III) and Fe(III) from ethanol was investigated at 25 ºC. The xerogel adsorption capacities were obtained from the adsorption isotherms by using the batch method. Flame atomic absorption spectrometry (FAAS) was used to estimate the concentration of metal ions in solution. The adsorption affinity follows the series Cr(III) > Fe(III) > Al(III) and the maximum adsorption capacities of the metal ions were 0.61, 0.52 and 0.43 mmol g-1, respectively.

The xerogel p-anisidinepropylsilica was obtained. This solid presents some residual paraffin and also a small fraction of high organofunctionalized material that was leached in polar solvent. The xerogel purification could be achieved by exhaustively washing with hexane and dichloromethane solvents, or submitting the xerogel to thermal treatment up to 300 ºC, in vacuum. The resulting purified xerogel material present an appreciable thermal stability and resistance to leaching by solvents.